Fabrication and Characterization of Vapor Gown Carbon Fiber/304L Matrix Stainless Steel Composite by Spark Plasma Sintering

In this paper, VGCF/304L stainless steel composite was prepared using spark plasma sintering (SPS) with 2 vol.% nanocarbon fiber. Then, phase content, grain size, and mechanical properties were evaluated. The results showed that the Vickers hardness of 304L sintered stainless steel and the composite prepared by SPS under the condition of 950 °C for 10 min were 244 HV and 310 HV, respectively, which is an increase of about 27.0%. The yield strength ascended from 587.1 MPa to 890.2 MPa, registering an increase of approximately 51.6%. Concurrently, the ultimate tensile strength rose from 821.5 MPa to 1064.7 MPa, with an approximate increase of 29.6%. This method for improving the mechanical properties of stainless steel is expected to be widely adopted for producing fiber-reinforced metal matrix composites with excellent overall performance.