High temperature deformation of polycrystalline C40 Mo(Si,Al)2

Polycrystalline Mo(Si,Al)2 with C40 crystal structure was deformed in compression with a strain rate of 10−4 s−1 at 1300 °C. The specimens were deformed to a strain of 10%–15% and showed maximum stresses around 150 MPa prior to pronounced softening. No crack formation or significant increase in porosity could be observed. Post-test microstructure analysis revealed that the material was inhomogeneously deformed on both inter- and intragranular levels. Dynamic recrystallization occurred alongside low angle grain boundary formation in highly deformed grains. Furthermore, complex intragranular deformation fields suggest that slip systems other than 21̄1̄0[0001] may be active during deformation.