Mechanical Properties of Recycled Concrete Containing Brick–Concrete Waste Aggregates with Basalt Fiber-Reinforced Polymer (BFRP) Fibers

With the advancement of urbanization, recycled aggregate concrete derived from construction waste has received increasing research attention. This study primarily focuses on a novel method to enhance the mechanical properties of recycled aggregate concrete derived from brick–concrete waste by mixing short-cut BFRP fibers. A series of experimental tests, including an axial compression test, a splitting tensile test, and a bending test, were conducted on specimens of RBCAC (recycled brick–concrete aggregate concrete) with different brick–concrete ratios and BFRP fiber contents. The effects of the brick–concrete ratio and BFRP content on various mechanical properties were systematically investigated. The results indicate that the brick–concrete ratio significantly affects the mechanical properties of RBCAC. The compressive strength decreased by approximately 2.0–4.7% as the brick-to-aggregate ratio increased from 0.25 to 4, with the peak strength (34.3 MPa) occurring at a ratio of 0.67. In addition, a strong linear relationship was observed between the compressive strength and other mechanical properties of BFRP-RBCAC. Based on the experimental data, the existing constitutive model for recycled concrete was modified by introducing a brick–concrete ratio correction factor and a fiber reinforcement factor. The proposed compression constitutive model is suitable for recycled brick–concrete aggregate concrete incorporating hybrid BFRP fibers.