[Influence of EPS on silicate corrosion inhibition for copper pipe in soft water].

The effects of sodium alginate on silicate corrosion inhibition for copper pipe in simulated soft water were investigated. The results showed that more soluble copper release was occurred when low concentration sodium alginate was in presence. The 1 a aged copper pipe released more soluble copper than the 3 a and 10 a aged copper pipe. The sequence of concentration of soluble copper release was c 1 a > c 3 a, > c 10 a. However, compared to the low concentration sodium alginate, soluble copper released from the 1 a aged copper pipe increased, and the 3 a and 10 a aged copper pipe were inverse when high level sodium alginate was in presence. These phenomena showed that the effect of silicate corrosion inhibition decreased when extracellular polymer substances was dissolved in soft water. Under the conditions of pH 7.5 and sodium alginate 16 mg/L, soluble copper release tend was gradually increase-decrease-gradually run-up which due to the absorption of sodium alginate on the surface of copper surface and the complex interaction between sodium alginate, silicate and copper ions. When the initial pH value was low, compared to the system of no sodium alginate, the soluble copper release distinctly increased in the presence of sodium alginate. The amount of soluble copper released from 1 a copper pipe is higher than that from 3 a and 10 a aged copper pipe, which due to the different components of copper corrosion by-products on the surface of different aged copper pipes and the different solubility of different corrosion by-products.