Evaluation of mechanical, optical, and fluoride‐releasing properties of a translucent bulk fill glass hybrid restorative dental material

OBJECTIVE: Measure and compare the mechanical properties, translucency, and fluoride-releasing capabilities of EQUIA Forte HT against Fuji IX GP and ChemFil Rock. MATERIALS AND METHODS: Ten specimens of each material were fabricated for compressive strength (CS), flexural strength (FS), and surface hardness analysis at 24 h and 7 days. The L*a*b* values were measured against a black-and-white background using a spectrophotometer to analyze the translucency parameter (TP). Fluoride release was recorded after 2 months of immersion in distilled water. The mean data was analyzed by 1- and 2-way ANOVA (α = 0.5). RESULTS: EQUIA Forte HT showed higher CS, surface hardness, and FS values (p < 0.05) compared with Fuji IX GIC, while no significant difference was found in FS values between EQUIA Forte HT and Chemfil Rock (p > 0.05). The EQUIA Forte HT exhibited significantly higher translucency in comparison to both ChemFil Rock (p < 0.001) and Fuji IX GICs (p < 0.05). An increase (p > 0.05) of fluoride release was observed for EQUIA Forte HT. CONCLUSION: The EQUIA Forte HT Glass-ionomer cements (GIC) offers enhanced translucency, improved strength, and enhanced fluoride-releasing properties compared to the traditionally used Fuji IX GIC and ChemFil Rock GICs. This material might have a wide range of clinical applications due to its improved strength and optical properties. CLINICAL SIGNIFICANCE: Glass-ionomer dental restorative materials possess unique advantageous characteristics. However, its poor mechanical and optical properties have typically limited its clinical applications. Efforts to improve these properties have resulted in enhanced GICs. EQUIA Forte HT GIC offers enhanced mechanical and optical properties with potential applications in posterior and anterior restorative procedures.