Kinetics of specific surface area change using the Boltzmann model

During sintering of the 2MgO-2Al2O3-5SiO2 system, cordierite, an attractive ceramic material because of its properties, is obtained. Effects of mechanochemical activation of stoichiometric mixtures, performed to investigate possibilities of lowering cordierite formation temperature during sintering, were monitored by thermogravimetric and differential thermal analyses. Specific surface areas of the mechanically activated powder mixtures were determined by the BET method. Kinetics of the specific surface area increase was analyzed using the Boltzmann model. It was confirmed that with activation time increase, temperatures of phase transformations were shifted to lower values and, according to FTIR analysis no significant changes occurred during material aging. According to the obtained results, it may be concluded that since mechanochemical activation has an influence on the treated powder mixture, lowering of the cordierite formation temperature during the sintering process is expected.