Nitrogen-rich carbon nitride as solid-phase microextraction fiber coating for high-efficient pretreatment of polychlorinated biphenyls from environmental samples

Abstract A two-dimensional nitrogen-rich carbon nitrogen (C3N5) material was prepared via a facile high temperature thermal polymerization. For the first time, the C3N5 was used as fiber coating of solid-phase microextraction (SPME) to extract and preconcentrate polychlorinated biphenyls (PCBs) before gas chromatography (GC) analysis. The X-ray diffraction, N2 adsorption-desorption, Fourier transform-infrared spectroscopy, thermogravimetric analysis, and X-ray photoelectron spectroscopy were performed to investigate structure, functional groups, thermal stability, bonding type, element composition, and atomic ratio of C3N5. The two-dimensional planar stacking structure was further verified by scanning electron microscopy and transmission electron microscopy. Five PCBs including PCB-4, PCB-12, PCB-29, PCB-52 and PCB-101 were selected as targets to evaluate performance of SPME fiber. Under the optimal conditions, the method showed a good linear range from 0.01 to 1000 ng/mL with the correlation coefficients (R2) higher than 0.9990. Enrichment factors of the method were obtained from 2045 to 3080. The limits of detection (LODs, S/N = 3) and limits of quantification (LOQs, S/N = 10) were calculated as 0.0031–0.0111 ng/mL and 0.01–0.05 ng/mL, respectively. The precisions of intra-day and inter-day were obtained with the relative standard deviations (RSDs) at 1.5–6.6% and 0.8–6.9%, respectively. The fiber-to-fiber producibility was achieved with RSDs ranged from 3.5% to 11.4%. The method was applied to detect PCBs in river water and soil samples. The contents were calculated at 0.040–0.147 ng/mL in water and 0.520–3.218 ng/g in soil. The C3N5 as SPME fiber coating material may be applied to extract and preconcentrate other environmental pollutants which have similar chemical structures with PCBs.