Thermal Conductivity of Magnesium Silicide Semiconductor Prepared from Rice Husk

The variation of thermal conductivity with temperature for magnesium silicide semiconductors prepared from rice husk by crucible ignition method and by alloying technique and sieved to various mesh sizes are measured in vacuum at a pressure of 0.133 Pa (10−3 Torr). It is seen that in the case of the material prepared by alloying technique the thermal conductivity is larger for larger grain size material and smaller for smaller grain size material. The behaviour tallies with the results obtained by Rowe and Bhandari. The material prepared by the crucible ignition method does not follow a definite trend because of the presence of a second phase material MgO in it. It is also seen that the thermal conductivity decreases with absolute temperature for all the cases. This phenomena is explained with the help of a theory given by Drabble and Goldsmid. Die Änderung der thermischen Leitfähigkeit mit der Temperatur wird für Magnesiumsilizidhalbleiter, die aus Reishülsen mit der Tiegelignitinmethode und durch Legierungstechnik hergestellt sowie mit unterschiedlichen Maschenweiten gesiebt werden, im Vakuum bei einem Druck von 0,133 Pa (10−3 Torr) gemessen. Für den Fall, daß das Material mit Legierungstechnik hergestellt wird, ist die thermische Leitfähigkeit größer für Material mit größerer Korngröße und kleiner für Material mit kleinerer Korngröße. Das Verhalten stimmt genau mit den von Rowe und Bhandari erhaltenen Ergebnissen überein. Das Material, das mit der Tiegelignitinmethode präpariert wird, folgt nicht einem definierten Trend aufgrund der Anwesenheit eines zweiten Phasenmaterials, MgO, darin. Es wird auch gezeigt, daß die thermische Leitfähigkeit in allen Fällen mit der absoluten Temperatur abnimmt. Dieses Phänomen wird mit Hilfe der Theorie von Drabble und Goldsmid erklärt.