Preparation of flexible and transparent polylactic acids films by crystallization manipulation

Abstract Highly flexible and transparent polylactic acids (PLAs) films were successfully prepared by manipulating their crystallization. The semicrystalline poly(L‐lactic acid) (L) was blended with a noncrystalline poly(DL‐lactic acid) (DL) together with diglycerol tetraacetate (DGTA). Optimal DGTA content to plasticize PLAs was about 17%. Addition of DL hindered the crystallization of the films. Tensile strengths of the films having DL content more than 5% were about 10 MPa while the elongations at break were boosted as DL content increased. Films having L/DL ratio of 50/50 showed elongations at break of 270%. Stretch ability and clarity of films containing 15–50% DL were fair although they were subjected to annealing at 60 °C for 1 h. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 6489–6495, 2008