Properties of polycarbonate/acrylonitrile‐butadiene‐styrene blends

Abstract To help make a good polymer blend by melt blending, the properties of polycarbonate (PC)/acrylonitrile‐butadiene‐styrene (ABS) systems with various compositions have been investigated. As ABS is blended into PC to form a binary system, Brabender torque is reduced, a phenomenon that results in Improved processability of PC. With increasing ABS content, the mechanical properties of the blends such as tensile strength, modulus, hardness, and shrinkage decrease. However, with the variation of composition, Izod impact strength shows a maximum, while elongation at break exhibits a minimum. These phenomena are discussed with dynamic viscoelasticities and scanning electron microscopic morphological results. The value of Δ T g ( T g β PC − T g β ABS ) is at its smallest when the ratio of PC to ABS is 90:10, However, the value rises with an increase in ABS because the butadiene content of the ABS hinders compatibility in the binary system. At the 90:10 composition, the damping height is optimal. In addition, the dispersed phase of the ABS is most ideal, absorbing the impact force and showing high impact strength. Composition ratios other than 90:10 present high damping as well as undesirable phase separation because of poor adhesion between two phases. As a result, the mechanical properties are reduced.