High-Flux Nanofibrous Composite Reverse Osmosis Membrane Containing Interfacial Water Channels for Desalination

A nanofibrous composite reverse osmosis (RO) membrane with a polyamide barrier layer containing interfacial water channels was fabricated on an electrospun nanofibrous substrate via an interfacial polymerization process. The RO membrane was employed for desalination of brackish water and exhibited enhanced permeation flux as well as rejection ratio. Nanocellulose was prepared by sequential oxidations of 2,2,6,6-tetramethylpiperidine-1-oxyl (TEMPO) and sodium periodate systems and surface grafting with different alkyl groups including octyl, decanyl, dodecanyl, tetradecanyl, cetyl, and octadecanyl groups. The chemical structure of the modified nanocellulose was verified subsequently by Fourier transform infrared (FTIR), thermal gravimetric analysis (TGA), and solid NMR measurements. Two monomers, trimesoyl chloride (TMC) and m-phenylenediamine (MPD), were employed to prepare a cross-linked polyamide matrix, i.e., the barrier layer of the RO membrane, which integrated with the alkyl groups-grafted nanocellulose to build up interfacial water channels via interfacial polymerization. The top and cross-sectional morphologies of the composite barrier layer were observed by means of scanning electron microscopy (SEM), atomic force microscopy (AFM), and transmission electron microscopy (TEM) to verify the integration structure of the nanofibrous composite containing water channels. The aggregation and distribution of water molecules in the nanofibrous composite RO membrane verified the existence of water channels, demonstrated by molecular dynamics (MD) simulations. The desalination performance of the nanofibrous composite RO membrane was conducted and compared with that of commercially available RO membranes in the processing of brackish water, where 3 times higher permeation flux and 99.1% rejection ratio against NaCl were accomplished. This indicated that the engineering of interfacial water channels in the barrier layer could substantially increase the permeation flux of the nanofibrous composite membrane while retaining the high rejection ratio as well, i.e., to break through the trade-off between permeation flux and rejection ratio. Antifouling properties, chlorine resistance, and long-term desalination performance were also demonstrated to evaluate the potential applications of the nanofibrous composite RO membrane; remarkable durability and robustness were achieved in addition to 3 times higher permeation flux and a higher rejection ratio against commercial RO membranes in brackish water desalination.