In Situ Thermal Interactions of Cu-Based Anti-Corrosion Coatings on Steel Implemented by Surface Alloying

Incorporating expensive alloying elements into bulk steel for corrosion protection is undesirable, considering that only the surfaces are exposed to aggressive environments. Therefore, this work focused on developing and optimizing a new surface functioning technology through in situ observation of thermal interactions between the metallic powders at elevated temperatures. The study revealed that the Cu-Ni powder mixture, with 12.5 wt% Ni, began to melt at 1099.5 °C and was fully melted at 1175 °C, significantly different from the Cu-Ni solid solution and bulk Cu or Ni. As a result of high-temperature reactions, copper penetration of up to 35 µm for pure copper and 55 µm for copper-chromium composite coatings occurred due to liquid metal corrosion. In contrast, the copper-nickel composite coating exhibited a cupronickel solution microstructure with FeNi dendrites and a nickel-rich transition layer. This cupronickel coating, with a chemical composition of 89.3 wt% Cu, 6.2 wt% Ni, and 4.5 wt% Fe, demonstrated uniform thickness, superior surface morphology, and continuous coverage on the steel substrate. Furthermore, the Ni-rich transition layer played a vital role in preventing copper penetration along the grain boundary of the steel matrix while forming a chemical binding between the coating and the substrate. The practicality of the coating was further confirmed through the hot-rolling procedure and subsequent electrochemical corrosion tests, which resulted in a 44% improvement in corrosion resistance.