Highly crystalline, low-ash, graphite from coal using an Fe2O3-based catalytic process with recovery and reuse of catalyst and process acid

ABSTRACT This study presents a sustainable process for producing highly crystalline, low-ash graphite from sub-bituminous coal using an Fe 2 O 3 -based catalytic method. The process integrates coal mineral removal, catalyst regeneration, and reagent recycling into a closed-loop system. Acid-soluble Fe-residue and mineral impurities are eliminated from the solid graphite through HCl treatment, followed by hydrolytic distillation to regenerate Fe 2 O 3 and recover HCl for reuse. Coal-derived silica is removed with a KOH rinse, yielding low-ash graphite suitable for high-performance applications. The closed-loop catalytic graphitization, where the recovered Fe 2 O 3 and HCl are used in subsequent graphitization runs, produces graphite with a degree of graphitization exceeding 95%. The L a and L c crystallite sizes reach 65–78 nm and 44–48 nm, respectively, with BET surface areas of 4–10 m 2 /g and an ash content below 0.1 wt.%. Lithium-ion battery testing reveals that anodes fabricated with this graphite deliver an initial discharge capacity between 384.5 and 421.2 mAh/g, averaging 395.0 ± 19.1 mAh/g, along with initial coulombic efficiencies of 85.0–89.1%. After 100 discharge–charge cycles at 0.25C, reversible capacities remain between 358.8 and 369.7 mAh/g, while coulombic efficiency stays above 99.9%. The findings highlight that coal can serve as a viable precursor for high-quality graphite production under relatively mild conditions, avoiding the need for extreme temperatures or aggressive reagents such as hydrofluoric acid, commonly employed in conventional processes. This work demonstrates both technical feasibility and environmental benefits, emphasizing its potential to support large-scale, sustainable graphite production for applications such as lithium-ion batteries.