Anodic behaviour of Zn0.5Al doped with molybdenum in acidic, neutral and alkaline media

The paper presents the results of a potentiodynamic study of the anodic behaviour of Zn0.5Al doped with molybdenum in the acidic (0.1 M, pH = 1; 0.01 M, pH = 2; 0.001 M, pH = 3), neutral (0.03, 0.3, 3%, pH = 7) and alkaline (0.001 M, pH = 10; 0.01 M, pH = 11; 0.1 M, pH = 12) media of HCl, NaCl and NaOH electrolytes. In the potentiodynamic mode with an electrode potential sweep rate of 2 mV/s, all Zn0.5Al-Mo samples containing from 0.01 to 1.0 wt% of molybdenum demonstrated a shift in the potentials of corrosion, pitting formation and repassivation. These potentials shift towards negative values in acidic and alkaline media, while shifting to positive values in a neutral medium. It was established that an increase in the concentration of electrolytes led to a shift of all the considered potentials towards negative values in all media - acidic, neutral and alkaline. This dependence is associated with the specific features of the process of anodic dissolution of alloys during the formation of an oxide film on their surface. The significance of the dependence of the stationary potential of free corrosion of alloys on time for establishing the passivity of surfaces in acidic, neutral and alkaline media was shown. It was determined that zinc alloys doped with molybdenum are resistant to pitting corrosion in all the investigated media. This resistivity is particularly high in acidic (0.001 M), neutral (0.03%) and alkaline (0.001 M) media of HCl, NaCl and NaOH electrolytes. The favourable effect of molybdenum on both the anodic behaviour of Zn0.5Al and the overall increase in the corrosion resistance of alloys was demonstrated. In comparison with undoped Zn0.5Al alloys, the corrosion rate of alloys doped with molybdenum (0.01-1.0 wt%) is 2-2.5 times lower. The proposed compositions of Zn0.5Al-Mo alloys can be used as noncorrosive coatings for steel products.