Layer-by-layer self-assembly of PLL/CPP-ACP multilayer on SLA titanium surface: Enhancing osseointegration and antibacterial activity in vitro and in vivo

Implants are expected to possess both excellent osteointegration and antibacterial activity because poor osseointegration and infection are two major causes of titanium implant failure. In this study, we constructed layer-by-layer self-assembly films consisting of anionic casein phosphopeptides-amorphous calcium phosphate (CPP-ACP) and cationic poly (L-lysine) (PLL) on sandblasted and acid etched (SLA) titanium surfaces and evaluated their osseointegration and antibacterial performance in vitro and in vivo. The surface properties were examined, including microstructure, elemental composition, wettability, and Ca2+ ion release. The impact the surfaces had on the adhesion, proliferation and differentiation abilities of MC3T3-E1 cells were investigated, as well as the material's antibacterial performance after exposure to the oral microorganisms such as Porphyromonas gingivalis (P. g) and Actinobacillus actinomycetemcomitans (A. a). For the in vivo studies, SLA and Ti (PLL/CA-3.0)10 implants were inserted into the extraction socket immediately after extracting the rabbit mandibular anterior teeth with or without exposure to mixed bacteria solution (P. g & A. a). Three rabbits in each group were sacrificed to collect samples at 2, 4, and 6 weeks of post-implantation, respectively. Radiographic and histomorphometry examinations were performed to evaluate the implant osseointegration. The modified titanium surfaces were successfully prepared and appeared as a compact nano-structure with high hydrophilicity. In particular, the Ti (PLL/CA-3.0)10 surface was able to continuously release Ca2+ ions. From the in vitro and in vivo studies, the modified titanium surfaces expressed enhanced osteogenic and antibacterial properties. Hence, the PLL/CPP-ACP multilayer coating on titanium surfaces was constructed via a layer-by-layer self-assembly technology, possibly improving the biofunctionalization of Ti-based dental implants.