Preparation and properties of glass fiber reinforced nylon56 composites

Abstract Glass fiber (GF) reinforced nylon56 composites (nylon56/GF) were prepared by melting and blending through twin‐screw extruder with continuous fiber feeding. The structure and properties of the composites were characterized by electron density tester, polarizing microscope, scanning electron microscope, electro‐mechanical universal testing machine and thermal analyzer. The results showed that the density of the prepared composites is less than 1.37 g/cm 3 . There is strong interface adhesion between glass fiber and nylon56 matrix in the composite system, and the glass fiber length in the system is 0.47–0.61 mm. With the increase in the content of high‐performance glass fiber, the mechanical properties of the composite are significantly improved. When four bundles of GF are added, the properties of the nylon56/GF composite are the best. The tensile strength of nylon56/GF composite reaches 160 MPa, 86.9% higher than that of nylon56. The bending strength is 180 MPa and increases by 98.7% more than that of nylon56. The flexural modulus is 7100 MPa and rises by 125.6% compared with nylon56, and the impact strength is 11 kJ/mm 2 , which is 307.4% higher than that of nylon56. The nylon56/GF composite has a low density and excellent performance and can be widely used in locomotive and wind power.