Fluorine-Free Dual Superamphiphobic Cellulose Paper Coated with Mushroom-like Pillar Microstructure

In this work, we report a unique and facile approach to the manufacture of fluorine-free superamphiphobic paper. Based on the principle that Fe3O4 nanoparticles (NPs) arranged along the direction of a magnetic field, the mixture of Fe3O4 NPs and polydimethylsiloxane (PDMS) was coated on kraft paper through self-assembly and thermal-curing at a high temperature in a magnetic field, fabricating a mushroom-like microstructure on the paper. At an Fe3O4 NPs content of 75%, the radius of the mushroom-like pillar caps (RCAP) and center-to-center spacing between two pillars (S) obtained the optimal size of 37 ± 18 μm and 237 ± 38 μm, respectively. The oil-contact angle and water-contact angle of the fabricated paper were up to 156° and 160.4°, respectively. It also showed excellent oleophobic stability; the oil-contact angle was still maintained at 141.9° after 1 h. In addition, the contact angles of milk, ethylene glycol and castor oil were all above 150°, and the contact angle of diiodomethane was 134.2°. Moreover, the sample showed great oil resistance with a kit rating value of 12/12 and permeability of 1800+ s.