Preparation and thermoelectric properties of PEDOT:PSS coated Te nanorod/PEDOT:PSS composite films

PEDOT:PSS coated Te (PCTe) nanorod/PEDOT:PSS composite films were prepared by a drop-casting technique. H2SO4 treatment was employed to enhance thermoelectric (TE) properties of the composite films. The addition of PCTe nanorods increased both the electrical conductivity and the Seebeck coefficient of the composite films. An optimized power factor of 141.9 μW/mK2 was obtained for the film containing 90 wt% PCTe nanorods treated with 12 M H2SO4 at room temperature, which was 2.75 times as high as that of the untreated composite film, corresponding to the electrical conductivity and Seebeck coefficient of 204.6 S/cm and 83.27 μV/K, respectively. XPS and GIWAXS analysis revealed the removal of insulating PSS units and the rearrangement of PEDOT chains after the H2SO4 treatment. Finally, a 9-leg TE generator prototype was fabricated using the optimized composite film. The maximum output power and area output power density produced from the prototype were 47.7 nW and 57.2 μW/cm2, respectively, at the temperature difference of 40 K.