지르코니아 코어의 종류와 도재 두께에 따른 색상의 변화

Purpose: This study focused on achieving desired shades by combining zirconia core with different thickness porcelain in order to make dental prostheses effectively.Materials: White and colored LAVATM All Ceramic (3M-ESPE, Seefeld, Germany), and Zirkonzahn (Bruneck, Italy) Trans and prettau were used to have Zirconia. LAVATM Ceram (3M-ESPE, Germany) and ICE (Zirkonzahn, Italy) powder were used to have the porcelain.Methods: Before Match: Stand sample each group 1.2 dentin sample L*, a*, b* value in every dentin and core sample Matched experimental groups: Same thickness dentin + different thickness coreSame thickness core + different thickness dentinResults: 1. All L , a , b indexes of zirconia core and porcelain veneer in LAVA group and Zirkonzahn group were different.2. When you combine the white zirconia core of LAVA group with a porcelain veneer, the thickness of the porcelain must be more than 0.5mm to meet the standard target.3. When all the colored zirconia cores of LAVA group were combined with porcelain veneers, there was no significant difference from the standard target.4. When the zirconia cores of Zirkonzahn group are combined with porcelain veneers, the thinner thicknesses were closer to the standard tab than thicker thicknesses; however, there was a significant difference in all combinations, with Delta E * value indicating more than 3.Conclusion: When it comes to colored zirconia, which is the most popular, the thicknesses of both a core and a dentin veneer must be more than 0.3 to get an appropriate shade. There is more possibility to get desirable shades when the thicknesses of a white core are thinner; however, they would be vulnerable to the environment and lose their color. When combine a zirconia core with a dentin veneer, using Zirkonzahn group needs more considerations in order to meet the standard target.