Mechanical, wear and corrosion behaviours of laser additive manufactured iron-based heterogeneous composite coatings for tillage tools

Steel is commonly used in engineering components, and it has a high tendency to wear and corrosion attacks when exposed to unfavourable working conditions. The use of chromium-vanadium-iron-rich carbide reinforced iron-based hard facings has become more important in improving the corrosion and wear resistance of such steel subjected to abrasive and impact conditions. In this study, the chromium-vanadium-iron carbide reinforced coatings were developed using in-situ by depositing FeCrV15+Cr powder through laser cladding on carbon steel. The influence of the reinforcement on the microstructure of the coating in relation to its laser processing condition and extra chromium addition was investigated. Furthermore, the effect of the coating's reinforcement on the hardness, microstructures, anti-corrosion, and anti-wear properties of the carbon steel used in tillage and mining operations was investigated. The result is a defect free deposits with a solid metallurgical attachment to the substrate and improved microhardness. FeCrV15 deposits had a wear-resistant (with a wear rate of 2.42 × 10−6 mm3/N/m) and anti-corrosion capability (with a corrosion rate of 0.001869 mm/yr) that were several folds higher than the steel substrate (with wear rate of 1.72 × 10−3 mm3/N/m and corrosion rate of 0.1168 mm/yr). The general grain refinement of the FeCrV15 deposits was richly enhanced in the iron base matrix. This resulted in outstanding wear and corrosion resistance attributed to the better production of VC–Cr3C2–Cr7C3 particles and better grain refinement of the microstructural formation.