Icephobicity of Hierarchically Rough Aluminum Surfaces Sequentially Coated with Fluoroalkyl and PDMS Alkoxysilanes

Superhydrophobic surfaces fabricated by grafting 1H,1H,2H,2H-heptadecafluorodecyl trimethoxysilane (FD-TMS) and polydimethylsiloxane triethoxysilane (PDMS-TES) onto a nano-micro hierarchical aluminum (Al) surface are considered to possess substantial anti-icing functionality, with delayed freezing and low ice-adhesion strength (IAS). Verifying the impacts of PDMS and the synergism of PDMS and FD on the anti-icing performance is the goal of this study. Roughness, one of the prerequisites for superhydrophobicity, was obtained by etching Al substrates in aqueous HCl, followed by immersion in boiling water. FD-TMS and PDMS-TES were then coated on the rough Al substrates layer by layer; a congener coated with a single layer was also prepared for comparison. The FD-PDMS1.92 (1.92 wt.%) coating, in which FD-TMS and PDMS-TES were used as primary and secondary coating materials, respectively, exhibited superior icephobicity, with the lowest IAS of 28 kPa under extremely condensing weather conditions (−20 °C and 70% relative humidity, RH) and the longest freezing delay time of 230 min (at −18 °C). These features are attributed to the incorporation of a dense coating layer with a low-surface-tension FD and the high mobility of PDMS, which lowered the contact area and interaction between the ice and substrate. The substrate coated with FD-PDMS1.92 exhibited improved durability with an IAS of 63 kPa after 40 icing/melting cycles, which is far less than that achieved with the FD single-layer coating.