Reengineering the thermometric behaviors of Er3+/Yb3+-codoped Gd2Mo3O12 microparticles via dual-mode luminescence manipulation

Series of Er3+/Yb3+-codoped Gd2Mo3O12 (GMO:Er3+/2xYb3+) microparticles with dual-mode luminescence were fabricated with the assistance of sol-gel method. The phase structure, morphological information, upconversion (UC) and down-shifting luminescence properties of the final products were systematically investigated. At 980 nm light irradiation, strong UC emissions rise in all the products and their intensities depend on the dopant concentration, where the optimum status occurs at x = 0.25 and the two-photon capture procedure results in the UC emission mechanism. Besides, excited at 378 nm, the down-shifting photoluminescence is also gained in resulting samples. By means of the fluorescence intensity ratio technique, the thermometric properties of the studied samples were investigated through analyzing the diverse thermal quenching features of the green emissions from thermally coupled levels of Er3+. When the UC emission is selected, the maximum absolute and relative sensitivities of the GMO:Er3+/2xYb3+ microparticles are 0.0076 and 1.15% K−1, respectively, whereas they shift to 0.0036 and 0.89% K−1, respectively, when the down-shifting photoluminescence is adopted. Note that, the sensor sensitivities of developed microparticles are related to the luminescence mode, while they do not depend on Yb3+ content. These results suggest that the GMO:Er3+/2xYb3+ microparticles are promising thermosensitive luminescent materials for optical thermometry and their thermometric features can be tuned through changing luminescence mode.