Structure and Characteristics of the Metal of the Cr-Ni-Mo-Mn-Si-Ti-Nb System Obtained by Surfacing with a Flux-Cored Wire Alloyed by Boron Carbide

This study explores structure and characteristics of the nickel-chrome steel of the Cr-Ni-Mo-Mn-Si-Ti-Nb-B doping system obtained by surfacing with a flux-cored wire alloyed by boron carbide. It has shown that the deposited metal has a composite structure consisting of a supersaturated with alloyed elements solid solution with an austenite-martensitic matrix and a eutectic component (Mo, Cr, Fe, Nb) 2 B in the form of sections along the boundaries of former austenite grains. Because of the significant content of ferrite-forming elements in the process of crystallization, a metastable δ-ferrite is formed in the weld metal in the form of differently oriented interlayers between the martensite rails. As a result of aging of such a deposited metal at 500 °C for 2 hours, the metastable ferrite undergoes decay at the interphase boundaries α/δ with the formation of the σ phase, which represents sharpened plates with the size of 300÷550 nm. Moreover, aging leads to hardening of the matrix by finely dispersed carboboride and intermetallic phases (Cr, Mo, Fe, Nb, Ti) 23 (С,В) 6 , (Fe, Cr, Si) 2 (Mo, Ti) и (Ni, Fe) 3 Ti, causing high levels of hardness and wear resistance. The usage of this wire as a surfacing material allows to increase significantly the operability and reliability of the stop valve parts, which work on abrasion in contact with corrosive medium.