Growth, crystal structures, and magnetic properties of Fe–As films grown on GaAs (111)B substrates by molecular beam epitaxy

We study epitaxial growth, crystal structures, and magnetic properties of Fe–As compound thin films grown on GaAs (111)B substrates at various values of the As4:Fe flux ratio γ, using molecular beam epitaxy. The samples grown at low As4 flux (γ = 0.3, sample A) show mainly a body-centered-cubic (bcc) crystal structure, exhibiting ferromagnetic properties similar to bcc Fe. Meanwhile, the Fe–As samples grown at medium γ (2.7–4.5, sample group B) comprise regions of Ni2In-type FeAs (a hexagonal crystal with lattice constants of a = 0.399 nm and c = 0.536 nm), which are grown at the bottom and interface with the GaAs buffer layer, and a layer of non-stoichiometric FeAs with a DO3 structure (a = 0.522 nm) formed on the top. The DO3-structure FeAs phase contains partially transformed regions, which are characterized by thin stripes in a scanning transmission electron microscopy image. Furthermore, in the sample grown with high γ = 8.5 (sample C), a hexagonal Fe–As crystal with a large in-plane lattice constant (a = 0.691 nm and c = 0.542 nm) and threefold screw axes are observed. None of these crystal structures of Fe–As compounds has ever been reported. While sample C shows no ferromagnetism, the samples in group B exhibit strong ferromagnetism with high Curie temperature TC above 400 K. These new ferromagnetic Fe–As compounds are promising for spintronic device applications.