Fatigue Crack Growth and Precipitation Characteristics of a High Zn-Containing Al-Zn-Mg-Cu Alloy with Various Typical Aging States

The fatigue crack growth of Al-Zn-Mg-Cu alloy can be adjusted by different aging treatments. In the present work, a high Zn-containing Al-Zn-Mg-Cu alloy was treated by single, double and triple stage aging treatments and typical T6, T79 and T77 states were selected by tensile properties. Fatigue crack growth under these aging states was tested and related fracture morphology and precipitation characteristics were observed. The results showed that fatigue crack growth resistance for the alloy was T6