Improvement of Thermal Shock Resistance Performance of High Alumina Ceramic Filter Support

Mullite-corundum multiphase ceramic materials were prepared at 1400°C for 2h with bauxite chamotte and clay clinker as raw material (size<74 μm), molded at pressure of 50 MPa. Effect of raw materials composition on sintering and themal shock resistance of composite were researched by measurements of apparent porosity, bending strength，thermal shock resistance and thermal expansion rates, and analysed by XRD and SEM. The results showed that the best weigh percentage of raw materials with better sintering and themal shock resistance are bauxite chamotte 50 wt%, clay clinker 50wt% for mullite-corundum multiphase ceramic materials. The test results for high temperature gas cleaning dust removal technology development and the application of the composite ceramic material has important application value.