Effect of functionalized carbon nanotube on cement mortar: From experiment to DFT research

In this paper, functionalized nanotube-reinforced cementitious composites were prepared, and the mechanical property test results showed that the 28d flexural strength of the composite was increased by 41.58% at a hydroxylated carbon nanotube mass fraction of 0.08[Formula: see text]wt.% compared to the original cement mortar. Carboxylated carbon nanotubes with a mass fraction of 0.02%, on the other hand, increased the 28d compressive strength by 99.12%. Probing the effect of the presence of functional groups on carbon nanotubes on the CNT/C–S–H interface by first principles. The results showed that the shear strengths (11.392[Formula: see text]MPa and 14.130[Formula: see text]MPa) of hydroxylated carbon nanotubes and plain carbon nanotubes at the interface with cementitious (CNT-OH/CSH and CNT/CSH) were lower than the shear strengths (21.584[Formula: see text]MPa) of carboxylated carbon nanotubes at the interface with cementitious (CNT-COOH/CSH). The adsorption of functional groups on carbon nanotubes changes the electron distribution on the surface of carbon nanotubes. The introduction of carboxyl groups exacerbates the charge transfer between carbon nanotubes and cementitious groups and promotes the generation of solid chemical bonds. This is the reason that carboxylated nanotubes added as reinforcement to cement mortar give better strength to the composite than hydroxylated nanotubes.