Influence of Different Types of Fillers on the Performance of PMMA-Based Low-Temperature Rapid Repair Mortar

In order to further optimize the performance of PMMA (Polymethyl Methacrylate) repair mortar. In this paper, fly ash, talcum powder and wollastonite powder are used as fillers to modify the PMMA repair mortar. The effects of these three fillers on the working performance, mechanical performance and durability of PMMA repair mortar were explored. The study shows that the three fillers have good effect on the bond strength of the repair mortar, in which the fly ash has the best effect on the mechanical performance. The mechanical properties of PMMA repair mortar were best when the amount of fly ash was 60 phr (parts per hundred, representing the amount of the material added per hundred parts of PMMA). At this time, the 28 d compressive strength was 71.26 MPa and the 28 d flexural strength was 28.09 MPa, which increased by 13.31% and 15.33%, respectively. Wollastonite powder had the least negative effect on the setting time of the PMMA repair mortar. When the dosage of wollastonite powder was increased to 100 phr, the setting time was only extended from 65 min to 94 min. When the talc dosage was 60 phr, the best improvement in salt freezing resistance was achieved. After 100 cycles of salt freezing, the mass loss rate and strength loss rate decreased to 0.159% and 4.97%, respectively, which were 75.1% and 37.7% higher than that of the control group. The addition of all three fillers reduced the porosity and the proportion of harmful pores in the mortar. This study contributes to a comprehensive understanding how different types of fillers affect PMMA repair mortars, and it also provides theoretical support for the further development of low-temperature rapid repair mortars.